OBJECTIVE: Chemical solutions have been widely used for disinfection of dentures, but their effect on color stability of denture tooth acrylic resins after repeated procedures is still unclear. The aim of this in vitro study was to evaluate whether repeated cycles of chemical disinfectants affected the color stability of two denture tooth acrylic resins. MATERIAL AND METHODS: Sixty disc-shaped specimens (40 mm x 3 mm) were fabricated from two different brands (Artiplus and Trilux) of denture tooth acrylic resin. The specimens from each brand (n=30) were randomly divided into 6 groups (n=5) and immersed in the following solutions: distilled water (control group) and 5 disinfecting solutions (1% sodium hypochlorite, 2% sodium hypochlorite, 5.25% sodium hypochlorite, 2% glutaraldehyde, and 4% chlorhexidine gluconate). Tooth color measurements were made by spectrophotometry. Before disinfection, the initial color of each tooth was recorded. Further color measurements were determined after subjecting the specimens to 7, 21, 30, 45, 60, and 90 immersion cycles in each tested solution. Color differences (ΔE*) were determined using the CIE L*a*b* color system. Data were analyzed using two-way repeated measures analysis of variance (ANOVA) followed by Tukey tests. The significance level was set at 5%. RESULTS: There were statistically significant differences in ΔE* among the 5 disinfectants and water during the 90 cycles of immersion for both denture tooth acrylic resins. Distilled water promoted the greatest color change in both denture tooth acrylic resins, nevertheless none of tested disinfectants promoted ΔE* values higher than 1.0 on these acrylic materials during the 90 cycles of disinfection. CONCLUSIONS: Repeated immersion cycles in disinfecting solutions alter ΔE* values, however these values do not compromise the color of the tested denture tooth acrylic resins because they are imperceptible to the human eye.

This in vitro study evaluated the tensile bond strength of glass fiber posts (Reforpost - Angelus-Brazil) cemented to root dentin with a resin cement (RelyX ARC - 3M/ESPE) associated with two different adhesive systems (Adper Single Bond - 3M/ESPE and Adper Scotchbond Multi Purpose (MP) Plus - 3M/ESPE), using the pull-out test. Twenty single-rooted human teeth with standardized root canals were randomly assigned to 2 groups (n=10): G1- etching with 37% phosphoric acid gel (3M/ESPE) + Adper Single Bond + #1 post (Reforpost - Angelus) + four #1 accessory posts (Reforpin - Angelus) + resin cement; G2- etching with 37% phosphoric acid gel + Adper Scotchbond MP Plus + #1 post + four #1 accessory posts + resin cement. The specimens were stored in distilled water at 37°C for 7 days and submitted to the pull-out test in a universal testing machine (EMIC) at a crosshead speed of 0.5 mm/min. The mean values of bond strength (kgf) and standard deviation were: G1- 29.163 ± 7.123; G2- 37.752 ±13.054. Statistical analysis (Student's t-test; a=0.05 showed no statistically significant difference (p<0.05) between the groups. Adhesive bonding failures between resin cement and root canal dentin surface were observed in both groups, with non-polymerized resin cement in the apical portion of the post space when Single Bond was used (G1). The type of adhesive system employed on the fiber post cementation did not influence the pull-out bond strength.